Vacuum Melt Alloys

Vacuum Melt Alloy

Nickel Base Equiax
Nickel Base Equiax
Nickel Base Equiax	C	Cr	Ni	Co	Mo	W	Nb / Cb	Ta	Ti	Al	B	Zr	Hf	Fe	Re	Other	Density gm/cm³	Density lb/in³	Approximate Melting Range °F	Approximate Melting Range °C
B 1900	0.10	8	Bal	10	6	-	-	4.25	1	6	0.015	0.07	-			-	8.22	0.297	2325-2375	1274-1302
B 1900 +HF	0.10	8	Bal	10	6	-	-	4.25	1	6	0.015	0.1	1.1			-	8.25	0.298	-
B 1910	0.15	10	Bal	10	3	-	-	7.25	1.25	6	0.015	0.1	-			-	-		2400	1316
CM 681 LC®	.1	5.5	Bal	9	-	8.5	-	6	.15	-	-	.01	1.5	5.75	3	-	8.91	0.322	-	-
NI - X	.10	21.75	Bal	1.5	9	0.6	-	-	-	-	-	-	-	18.5		1.0xMn 1.0xSi	8.21	0.296	2300-2470	1260-1354
IN 100	0.16	10	Bal	15	3	-	-	-	4.75	5.5	0.015	0.04	-			.8V	7.75	0.280	2350-2435	1288-1335
IN 625	0.20	21.6	BAl	-	8.7	-	3.9	-	0.2	0.2	-	-	-			-	8.44	0.305	2350-2460	1288-1349
IN 713 C	0.10	13.5	BAl	-	4.5	-	2	-	0.8	6	0.010	0.06	-			-	7.91	0.286	2300-2350	1260-1288
IN 713 LC	0.06	12	Bal	-	4.3	-	2	-	0.7	5.8	0.007	0.06	-			-	8.00	0.289	2350-2410	1288-1321
IN 718	0.05	19	52.5	-	3	-	5	-	0.9	0.55	0.005	-	-	Bal			8.22	0.297	2300-2450	1260-1343
IN 738 LC	0.09	16	Bal	8.5	1.7	2.5	0.8	1.7	3.5	3.5	0.010	0.05	-			-	8.11	0.293	2250-2400	1231-1316
IN 738 C	0.17	16	Bal	8.5	1.7	2.5	0.8	1.7	3.5	3.5	0.010	0.1	-			-	8.11	0.293	-
IN 792	0.12	12.4	Bal	9	1.9	3.8	-	3.9	4.5	3.1	0.020	0.1	-			-	8.25	0.298	-
IN 792+Hf	0.11	12.2	Bal	9	2	3.8	-	4	4	3.5	0.015	0.1	.50 - .85			-	-		2270-2400	1240-1315
IN 939	0.15	22.4	BAl	19	-	1.6	1	1.4	3.7	1.9	0.010	0.1	-			-	8.17	0.295	2255-2440	1235-1338
Mar M 002*	0.15	9	Bal	10	-	10	-	2.5	1.5	5.5	0.015	0.05	1.5			-	8.53	0.308	-
Mar M 004	0.05	12	Bal	-	4.5	-	2	-	0.6	5.9	0.015	0.05	1.3			-	8.02	0.290	2425	1329
Mar M 200	0.15	9	Bal	10	-	12.5	1.8	-	2	5	0.015	0.05	-	-	-	-	8.53	0.308	2400-2500	1315-1370
Mar M 246	0.15	9	Bal	10	2.5	10	-	1.5	1.5	5.5	0.015	0.05	-			-	8.44	0.305	2400-2450	1315-1343
Mar M 247*	0.16	8.2	Bal	10	0.6	10	-	3	1	5.5	0.015	0.05	1.5			-	8.54	0.308	2380-2490	1305-1365
Mar M 421	0.15	15.5	Bal	9.5	2	3.8	2	-	1.8	4.3	0.015	0.05	-			-	8.08	0.292	2350-2450	1288-1343
CM 247 LC*	0.07	8	Bal	9	0.5	10	-	3.2	0.7	5.6	0.015	0.01	1.4			-	8.54	0.308	-
CM 681 LC																	8.91	0.322
Rene' 41	0.09	19	Bal	11	9.75	-	-	-	3.15	1.65	0.005	-	-			-	8.25	0.298	2400-2500	1315-1371
Rene' 77	0.07	14.6	Bal	15	4.2	-	-	-	3.3	4.3	0.015	0.04	-			-	7.91	0.286	2200-2550	1204-1400
Rene' 80	0.16	14	Bal	9.5	4	4	-	-	5	3	0.015	0.03	-			-	8.16	0.295	-
Rene' 95	0.15	14	Bal	8	3.5	3.5	3.5	-	2.5	3.5	0.010	0.05	-			-	8.19	0.296	-
Rene' 125	0.11	9	Bal	10	2	7	-	3.8	2.5	1.4	0.017	0.05	-			-	8.53	0.308	-
Rene' 220	0.02	18	Bal	12	3	-	5	3	1	0.5	0.010	-	-			-	-		2280-2455	1250-1350
U 500	0.07	19	Bal	18	4	-	-	-	3	3	0.007	-	-			-	8.02	0.290	-
U 700	0.07	15	Bal	18.5	5	-	-	-	3.5	4.4	0.025	-	-			-	7.91	0.286	2200-2550	1204-1400
Waspaloy	0.07	19.5	Bal	13.5	4.25	-	-	-	3	1.35	0.005	-	-			-	8.19	0.296	2425-2475	1329-1357
C263	0.06	20	Bal	20	5.9	-	-	-	2.15	0.45	0.001	-	-			-	8.36	0.302	-
C 1023	0.16	15.5	Bal	10	8.5	-	-	-	3.6	4.2	0.006	-	-			-	-		-
GMR 235	0.15	15.5	Bal	-	5.3	-	-	-	2	3	0.060	-	-	10		.3 Mn, .6 Si	8.00	0.289	-
GTD 111	0.10	14	Bal	9.5	1.6	3.8	-	2.8	4.9	3	0.012	0.02	-			-	8.17	0.295	-
GTD 222	0.10	22.5	Bal	19	-	2	0.8	1	2.3	1.2	0.005	0.012	-			-	-		2355-2500	1290-1370
* Also used as DS

Nickel Base Directionally Solidified

Nickel Base DS C Cr Ni Co Mo W Nb/Cb Ta Ti Al B Zr Hf Fe Re Other Density gm/cm³ Density lb/in³ Approximate Melting
Range °F Approximate Melting
Range °C

Mar M 200+Hf 0.14 9 Bal 10 - 12 1 - 2 5 0.015 - 0.8-1.9 - 8.61 0.311 -

Mar M 002 0.15 9 Bal 10 - 10 - 2.5 1.5 5.5 0.015 0.05 1.5 - 8.53 0.308 -

Mar M 247 0.16 8.2 Bal 10 0.6 10 - 3 1 5.5 0.015 0.05 1.5 - 8.54 0.308 -

PWA 1426 0.10 6.5 Bal 12 2 6 - 4 - 6 0.015 0.03 1.5 3 8.60 0.310 -

Rene' 142 0.12 6.8 Bal 12 2 5 - 6 - 6.2 0.015 0.02 1.5 3 8.60 0.310 -

CM 186 LC* 0.07 6 Bal 9 0.5 8 - 3 0.7 5.7 0.015 0.005 1.4 3 8.70 0.314 2400-2520 1315-1380

CM 247 LC 0.07 8 Bal 9 0.5 10 - 3.2 0.7 5.6 0.015 0.01 1.4 - 8.54 0.308 2385-2510 1310-1375

Rene' 80 H 0.16 14 Bal 9 4 4 - - 4.7 3 0.015 0.01 0.8

GTD 111 M 0.10 14 Bal 9.5 1.6 3.8 - 2.8 4.9 3 0.012 - -

*Also used as single crystal

Nickel Base Single Crystal

Nickel Base Single Crystal C Cr Ni Co Mo W Nb/Cb Ta Ti Al B Zr Hf Fe Re Other Density gm/cm³ Density lb/in³ Approximate Melting
Range °F Approximate
Melting
Range °C

PWA 1480 - 10 Bal 5 - 4 - 12 1.5 5 0.003 - - - 8.70 0.314 2350-2450 1290-1340

PWA 1484 - 5 Bal 10 1.9 5.9 - 8.7 - 5.65 - - 0.1 3 8.95 0.323 -

PWA 1487 - 5 Bal 10 1.9 5.9 8.4 5.65 0.25 3 Y 0.013 8.95 0.323

Rene' N4 - 10 Bal 8 2 6 0.5 5 3.5 4.2 - - 0.2 8.56 0.309 -

Rene' N5 - 7 Bal 8 2 5 - 6 - 6.2 - - 0.2 3 8.63 0.312 -

Rene' N6 - 4 Bal 12 1 6 - 7 - 5.8 - - 0.2 5 8.97 0.324 -

CMSX-2 - 8 Bal 5 0.6 8 - 6 1 5.6 - - - 8.56 0.309 2415-2500 1320-1370

CMSX-3 - 8 Bal 5 0.6 8 - 6 1 5.6 - - 0.1 8.56 0.309 2420-2510 1325-1375

CMSX-4 - 6.5 Bal 9 0.6 6 - 6.5 1 5.6 - - 0.1 3 8.70 0.314 2415-2515 1320-1380

CMSX-4 [ULS][La+Y] - 6.5 Bal 9 0.6 6 - 6.5 1 5.6 - - 0.1 3 La+Y 0.002 8.70 0.314

CMSX-4 (B/C)[MK4] 0.04 6.5 Bal 9 0.6 6 - 6.5 1 5.6 0.006 - 0.2 3 8.70 0.314

CMSX-6 - 10 Bal 5 3 - - 2 4.7 4.8 - - 0.1 7.98 0.288 -

CMSX-10K - 2 Bal 3 0.4 5 0.1 8 0.2 5.7 - - 0.03 6 9.05 0.327 2480-2575 1360-1410

CMSX-10N - 1.5 Bal 3 0.4 5 0.05 8 0.1 5.8 - - 0.03 7 2480-2575 1360-1410

CMSX 486 0.07 5 Bal 9 0.7 9 - 4.5 0.7 5.7 0.015 0.005 1 3 8.85 0.319 -

SRR 99 - 8 Bal 5 - 10 - 3 2.2 5.5 - - - - 8.56 0.309 -

RR 2000 - 10 Bal 15 3 - - - 4 5.5 - - - 1 V 7.87 0.284 -

AM 1 - 8 Bal 6 2 6 - 9 1.2 5.2 - - - - 8.59 0.310 -

AM 3 - 8 Bal 6 2 5 - 4 2 6 - - - - 8.25 0.298 -

SC 180 - 5 Bal 10 2 5 - 8.5 1 5.2 - - 0.1 3 8.84 0.319 -

Cobalt Base

Cobalt Base C Cr Ni Co Mo W Nb/Cb Ta Ti Al B Zr Hf Fe Re Other Density gm/cm³ Density lb/in³ Approximate Melting
Range °F Approximate
Melting Range °C

FSX-414 0.25 29 10 Bal - 7.5 - - - - 0.010 - - - 8.30 0.300 - -

Mar-M-302 0.85 21.5 - Bal - 10 - 9 - - 0.005 0.2 - - 9.21 0.332 - -

Mar-M-509 0.60 23 10 Bal - 7 - 3.5 0.2 - - 0.5 - - 8.85 0.319 2415-2525 1320-1385

Mar-M-918 0.05 20 20 Bal - - - 7.5 - - - 0.1 - - - -

HS 21 0.25 27 3 Bal 5 - - - - - - - - 1 0.6 Mn, 0.6 Si - -

HS 31 (X-40) 0.50 25 10 Bal - 7.5 - - - - - - - 1.5 0.5 Mn, 0.5 Si 8.60 0.310 -

X-45 0.25 25.5 10.5 Bal - 7 - - - - 0.010 - - - 8.60 0.310 -

HS 25 (L-605) 0.10 20 10 Bal - 15 - - - - - - - - 9.13 0.330 -

Haynes 188 0.10 22 22 Bal - 14 - - - - - - - 0.04 La 9.13 0.330 -

AiResist 13 0.45 21 - Bal - 11 2 - - 3.5 - - - 0.1 Y - -

AiResist 213 0.18 19 - Bal - 4.7 - 6.5 - 3.5 - 0.15 - 0.1 Y - -

AiResist 215 0.35 19 - Bal - 4.5 - 7.5 - 4.3 - 0.13 - 0.17 Y - -

F-75 0.25 28 - Bal 5.5 - - - - - - - - - 8.29 0.299 -

WI-52 0.45 21 - Bal - 11 2 - - - - - - 2 8.88 0.321 -

ECY 768 0.60 23 10 Bal - 7 - 3.5 0.2 - - - - - - -